Iron Oxide Red 130

Fe2O3/Fe3O4≥%96

Water soluble salts ≤%0.3

Residue on 45um ≤%0.2

PH-value 3.5-8

Oil absorption 15-25 

Density approx / cm3: 5.0-5.1

Iron oxide Red 190

Fe2O3/Fe3O4≥%95

Water soluble salts ≤%0.3

Residue on 45um ≤%0.2

PH-value 3.5-8

Oil absorption 15-25

Density approx / cm3 5.0-5.1

Iron oxide Brown 

Fe2O3/Fe3O4≥%92

Water soluble salts ≤%0.5

Residue on 45um ≤%0.3

PH-value 4-7

Oil absorption 20-30

Density approx / cm3 4.8

Iron Oxide black

Fe3O4: ≥95//≥90//≥95//≥93 

Oil absorption (%): 15-25 

Residue on bolted (%): ≤0.4 

Water soluble: ≤2.0 

Moisture (%): ≤1.0 

PH-value: 5-7 

Density: 0.9-1.2 

Particle Shape: spherical 

Color difference vs standard: ≤1 

Tinting strength (%): 95-105 

Character: 

1. Black powder, strong tinting and covering 

2. Lightness alkali resistant, only dissolved in heat strong acid 

Application: 

1.Industry coating,strong antirust 

2. Pigment of watercolour and grease-paint 

3. Tinting of the scagliola and concrete floor 

4. material of the magnetic steel in telecommnication

Iron oxide yellow 

Fe2O3: ≥85  

Oil absorption (%): 15-25 

Residue on bolted (%): ≤0.3 

Water soluble: ≤0.5 

Moisture (%): ≤1.0 

PH-value: 3-7 

Density: 0.9-1.4 

Particle Shape: spherical 

Color difference vs standard: ≤1 

Tinting strength (%): 95-105 

Character: 

1.Birght colorof brown yellow 

2.Lightfastness, heat-resistant, alkali resistant 

3.Becomes red pigment over 150℃ 

Application: 

1.Coating,paint,scagliola,tinting of the wall,floor 

2. Pigment of watercolour and grease-paint 

3. Tinting of the leather-colorant

Iron Oxide Blue

Application: 

Tinting presswork such as coating, print-ink, paint, crayonType: F100/F90 

Residue on bolted (%): ≤0.3 

Water soluble: ≤0.1 

Moisture (%): ≤1.0 

PH-value: 3-7 

Density: 0.4-0.8 

Particle Shape: In-regular 

Color difference vs standard: ≤1 

Tinting strength (%): 95-105

SAME ITEM OF ABOVE:

105°C Moisture ≤%1.0

Tinting strength % 95-105

Iron Oxide Green